дијаграм трансформације

presentation of austenite (3.12) transformation of ferrous materials in dependence of time and
temperature for a given steel composition
Note 1 to entry: Set of curves drawn in a semi-logarithmic coordinate system with logarithmic time/temperature
coordinates which define, for each level of temperature, the transformation of austenite as beginning and ending
the transformation to other phases (3.156).
Note 2 to entry: At the end of transformation, the amount of constituents of the microstructure and the hardness can be determined.

prezentacija transformacije austenita (3.12) materijala od gvožđa i čelika, u zavisnosti od vremena i temperature za za dati sastav čelika

NAPOMENA 1 uz termin: Niz krivih ucrtanih u polulogaritamski koordinatni sistem, logaritam vreme/
/temperatura, koje za svaku temperaturu definišu početak i kraj transformacije austenita u druge faze (3.156) u izotermalnim uslovima.

NAPOMENA 2 uz termin: Na kraju transformacije mogu da se očitaju količina i tvrdoća konstituenata mikrostrukture.

презентација трансформације аустенита (3.12) материјала од гвожђа и челика, у зависности од времена и температуре за за дати састав челика

НАПОМЕНА 1 уз термин: Низ кривих уцртаних у полулогаритамски координатни систем, логаритам време/
/температура, које за сваку температуру дефинишу почетак и крај трансформације аустенита у друге фазе (3.156) у изотермалним условима.

НАПОМЕНА 2 уз термин: На крају трансформације могу да се очитају количина и тврдоћа конституената микроструктуре.