temperatura transformacije stakla (Tg)

The transition of a glass from a rigid non-equilibrium state at low temperatures to a viscous liquid state at high temperatures is observed as an inflection in the expansion/temperature curve of the glass when heated at a constant rate. The transition temperature is defined as the temperature corresponding to the intersection of two tangents drawn from the lower temperature branch and the high-temperature branch of the dilatometer curve when the test-piece is heated at 5 K per minute (IEC 1006). NOTE At the glass transition temperature internal stresses are substantially removed within a few minutes, and the dynamic viscosity is approximately 10 12,3 Nsm–2

Prelaz stakla iz stanja krute neravnoteže na niskim temperaturama u viskozno tečno stanje na visokim temperaturama, uočen kao promena tačke infleksije krive širenja u funkciji temperature stakla kada se ono konstantno zagreva. Temperatura transformacije se definiše kao temperatura koja odgovara preseku dve tangente koje su povučene na donjoj i gornjoj grani temperature dilatometarske krive kada se ispitni komad zagreva 5 K u minuti (IEC 61006). NAPOMENA Na temperaturi transformacije stakla unutrašnja naprezanja se uklanjaju za nekoliko minuta, a dinamička viskoznost je oko 10 12,3 Nsm–2.

Prelaz stakla iz stanja krute neravnoteže na niskim temperaturama u viskozno tečno stanje na visokim temperaturama, uočen kao promena tačke infleksije krive širenja u funkciji temperature stakla kada se ono konstantno zagreva. Temperatura transformacije se definiše kao temperatura koja odgovara preseku dve tangente koje su povučene na donjoj i gornjoj grani temperature dilatometarske krive kada se ispitni komad zagreva 5 K u minuti (IEC 61006). NAPOMENA Na temperaturi transformacije stakla unutrašnja naprezanja se uklanjaju za nekoliko minuta, a dinamička viskoznost je oko 10 12,3 Nsm–2.