oxidation

result of the reaction of oxygen with iron and oxide-forming alloying elements in ferrous materials
Note 1 to entry: Oxide layers grow as temperature and time increase.
Note 2 to entry: Iron has three different oxides, wustite (FeO), magnetite (Fe3O4) and hematite (Fe2O3).
Note 3 to entry: There should be a distinction between oxidation as a result of an intentional oxidizing (3.151),
e.g. during oxynitriding (3.152), blueing (3.26) or after nitrocarburizing (3.144) or an unintentional effect by
carburizing (3.36) in oxygen containing carburizing media; see internal oxidation (3.124).

rezultat reakcije kiseonika sa železom i stvaranje legure postupkom oksidacije u materijalima od gvožđa i čelika

NAPOMENA 1 uz termin: Oksidni sloj se povećava sa porastom temperature i vremena.

NAPOMENA 2 uz termin: Železo ima tri različita oksida, vustit (FeO), magnetit (Fe3O4) i hematit (Fe2O3).

NAPOMENA 3 uz termin: Trebalo bi da postoji razlika između oksidacije kao rezultata namernog oksidisanja (3.151), npr. tokom oksinitriranja (3.152), površinske oksidacije na plavu boju (3.26), ili posle nitrokarburizinga (3.144), ili nenamernog uticaja naugljeničenja (3.36) u sredstvu za naugljeničenje koje sadrži kiseonik; videti unutrašnju oksidaciju (3.124).

резултат реакције кисеоника са железом и стварање легуре поступком оксидације у материјалима од гвожђа и челика

НАПОМЕНА 1 уз термин: Оксидни слој се повећава са порастом температуре и времена.

НАПОМЕНА 2 уз термин: Железо има три различита оксида, вустит (FeO), магнетит (Fe3O4) и хематит (Fe2O3).

НАПОМЕНА 3 уз термин: Требало би да постоји разлика између оксидације као резултата намерног оксидисања (3.151), нпр. током оксинитрирања (3.152), површинске оксидације на плаву боју (3.26), или после нитрокарбуризинга (3.144), или ненамерног утицаја наугљеничења (3.36) у средству за наугљеничење које садржи кисеоник; видети унутрашњу оксидацију (3.124).