hydrogen-induced cracking

HIC planar cracking that occurs in carbon and low alloy steels when atomic hydrogen diffuses into the steel and then combines to form molecular hydrogen at trap sites Note 1 to entry: Cracking results from the pressurization of trap sites by hydrogen. No externally applied stress is required for the formation of hydrogen-induced cracks. Trap sites capable of causing HIC are commonly found in steels with high impurity levels that have a high density of planar inclusions and/or regions of anomalous microstructure (3.16) (e.g. banding) produced by segregation of impurity and alloying elements in the steel. This form of hydrogen-induced cracking is not related to welding.

HIC

површинске прслине које се појављују у угљеничним и нисколегираним челицима онда када атоми водоника дифундују у челик и групишу се да би формирали молекуле водоника у међупростору

1. 1 уз термин:   Прслине су резултат стварања притиска изазваног водоником на местима међупростора. За формирање прслина изазваних водоником не захтева се примена напона споља. Места у међупростору која су у стању да узрокују HIC обично се налазе у челицима са високим нивоом нечистоћа који имају велику површинску густину нечистоћа и/или подручја са неправилном микроструктуром (3.16) (нпр. тракастом), насталом сегрегацијом нечистоћа и легирајућих елемената у челику. Овај начин стварања прслина изазваних водоником није повезан са заваривањем.