deformation temperature

DT
temperature at which the first signs of melting occur
Note 1 to entry: It is common that DT will occur shortly before HT/FT. If the test results show a small temperature
difference between SST and DT and a large temperature gap between DT and HT/FT it is advised that the analyst
review the images to verify if the temperature recorded as DT is truly due to melting or if it is a shape change
caused by excessive shrinkage.
Note 2 to entry: Deformation temperature can be seen as rounding of the edges, smoothing of surfaces, expansion
of the cylinder or general changing of the cylinder shape. If the test piece starts to swell or bubble without the
edges being rounded, the temperature is registered as DT (since swelling and bubbling only occur when a fraction
of the ash is melted).
Note 3 to entry: For computerized evaluation a shape factor change can be used to define the deformation
temperature. For definition of shape factor see Annex A.

DT

температура при којој се јављају први знаци појављивања топљења

1. 1 уз термин:   Уобичајено је да се DT појави непосредно пре HT/FT. Ако резултати испитивања покажу малу температурну разлику између SST и DT и велику температурну разлику између DT и HT/FT, онда се саветује да аналитичар преиспита слике како би верификовао да ли је температура забележена као DT заиста последица топљења или је у питању промена облика изазвана прекомерним омекшавањем.

НАПОМЕНА 2 уз термин:   Температура деформације се може посматрати као заокруживање ивица, изравнавање површина, ширење цилиндра или општа промена облика цилиндра. Ако испитна епрувета почне да бубри или испушта мехуриће, а ивице нису заобљене, онда се температура региструје као DT (пошто се бубрење и мехурићи јављају само онда када се део пепела отопи).

НАПОМЕНА 3 уз термин:   За компјутерско вредновање, промена фактора облика може да се користи за дефинисање температуре деформације. За дефиницију фактора облика видети Прилог А.